IndiaWILLSTRONG® CCP
Copper Composite Panel
WILLSTRONG® Copper Composite Panel (CCP) integrates the rich, evolving luster of authentic copper with the structural stability of a mineral-filled core. As time progresses, the copper surface gracefully matures from raw metallic sheen to warm dark brown, eventually forming a distinctive green patina that provides natural, lifelong protection against environmental corrosion.
Designed for high-end monumental architecture, luxury residential façades, and premium roof cladding, CCP offers unrivaled elegance, absolute surface flatness, and effortless processing without the prohibitive weight and cost of solid copper sheets.
Copper Composite Panel's authentic copper surface forms a protective patina, offering self-healing corrosion resistance and evolving aesthetics for decades.
With A2 mineral core, CCP provides high flexural strength and flatness, eliminating oil-canning and distortion typical of thin copper.
Copper composite panel uses a high-grade copper skin and a B1 flame-retardant advanced mineral core with effective smoke suppressant additives.
The panel gives excellent overall flatness, structural rigidity, sound insulation, and also B1 self-extinguishing properties with very low smoke emissions.
Copper composite panel is made of a thin copper layer and a lightweight polyethylene core that is also highly flexible.
It provides overall good flatness, also effective sound damping, adequate structural strength, and very low maintenance with long-lasting visual appeal.
Panel Thickness: 2.5mm, 3mm, 4mm, 5mm, 6mm
Metal Sheet Thickness | 0.3mm / 0.4mm / 0.5mm / 0.6mm / 0.8mm / 1.0mm | ||
Width | 1220mm | 1250mm | 1500mm |
Length | 1000-6000mm | ||
Natural Copper Series | √ | √ | √ |
Brass Series | √ | √ | √ |
Antique Series | √ | √ | √ |
Titanium Coating | √ | √ | √ |
Textured Series | √ | √ | √ |
Brushed Series | √ | √ | √ |
Mirror Series | √ | √ | √ |
Design | √ | √ | √ |
Special Finishes | √ | √ | √ |
Remark: Custom dimensions are available upon request
EU | EN13501-1 | A2-s1, d0 |
EU | EN13501-1 | B-s1, d0 |
Germany | DIN4102-7 | Passed |
Sigapore | BS476-Part 6 | Fire propagation index=1.0 |
Sigapore | BS476-Part 7 | Class 0 |
USA | NFPA285 | Passed |
USA | ASTM E84-15a | Flame Spread Index 5, Smoke Developed Index 0 |
China | GB 8624-2012 | A2-s1, d0 |
China | GB 8624-2012 | B-s1, d0 |
Russia | GOST31251 | Passed |
| THICKNESS | STANDARDS | UNIT | 3mm | 4mm | |||
|---|---|---|---|---|---|---|---|
| Fire-B1,S1,d0 | Fire-A2,S1,d0 | Fire-B1,S1,d0 | Fire-A2,S1,d0 | ||||
| Thickness of Copper Layers | mm | 0.3 | 0.3 | 0.5 | 0.5 | ||
| Weight | kg/m² | 6.2 | 6.5 | 8 | 8.3 | ||
| Width | mm | 1220/1250/1500 | 1220/1250/1500 | 1220/1250/1500 | 1220/1250/1500 | ||
| TECHNICAL PROPERTIES | |||||||
| Section modulus | W | cm³/m | 0.55 | 0.55 | 1.75 | 1.75 | |
| Rigidity | EJ | KNcm²/m | 1820 | 1820 | 3890 | 3890 | |
| Alloy/Temper of Copper Layers | T2 Pure Copper (M) / H62 Brass (Y2) | T2 Pure Copper (M) / H62 Brass (Y2) | T2 Pure Copper (M) / H62 Brass (Y2) | T2 Pure Copper (M) / H62 Brass (Y2) | |||
| Modulus of Elasticity | N/mm² | 115000 | 115000 | 115000 | 115000 | ||
| Tensile Strength of Copper | N/mm² | ≥205 | ≥205 | ≥205 | ≥205 | ||
| 0.2% Proof Stress | N/mm² | ≥70 | ≥70 | ≥70 | ≥70 | ||
| Elongation | % | ≥30 | ≥30 | ≥30 | ≥30 | ||
| Linear Thermal Expansion | 1.65mm/m at 100°C temperature | 1.65mm/m at 100°C temperature | 1.65mm/m at 100°C temperature | 1.65mm/m at 100°C temperature | |||
| CORE | Mineral filled polymer | Mineral filled polymer | Mineral filled polymer | Mineral filled polymer | |||
| SURFACE | Mirror / Brushed / Hammered / Patina Antique / Titanium Coated | Mirror / Brushed / Hammered / Patina Antique / Titanium Coated | Mirror / Brushed / Hammered / Patina Antique / Titanium Coated | Mirror / Brushed / Hammered / Patina Antique / Titanium Coated | |||
| Lacquering | Coil Coating Polyester (PET) | Coil Coating Polyester (PET) | Coil Coating Fluorocarbon(PVDF) | Coil Coating Fluorocarbon(PVDF) | |||
| Film Thickness | μm | ≥18 | ≥18 | ≥25 | ≥25 | ||
| Gloss(initial value) | 30-90 | 30-90 | 30-80 | 30-80 | |||
| Pencil Hardness | H-2H | H-2H | H | H | |||
| ACOUSTICAL PROPERTIES | |||||||
| Sound Absorption Factor | 0.05 | 0.05 | 0.05 | 0.05 | |||
| Sound Transmission Loss | db | ≥25 | ≥25 | ≥25 | ≥25 | ||
| THERMAL PROPERTIES | |||||||
| Thermal Resistance | R | m²k/w | 0.06 | 0.07 | 0.08 | 0.09 | |
| Thermal conductivity | w/mk | 0.47 | 0.45 | 0.42 | 0.4 | ||
| Heat transition coefficient | U | w/m²k | 5.8 | 5.75 | 5.65 | 5.58 | |
| Temperature Resistance | °C | -10 / 40 | -10 / 40 | -50 / 80 | -50 / 80 | ||
Color difference (ΔE) | ≤ 1.5 (within same batch) |
Impact resistance | ≥50kg.cm |
Pencil hardness | ≥2H |
Peel strength | ≥70 N/mm |
Tensile strength | ≥100 MPa |
Resistance to hydrochloric acid | No blistering, peeling, fading, or delamination; ΔE ≤ 1.5 |
Resistance to nitric acid | No swelling, discoloration, flaking, or copper exposure |
Solvent resistance | ≥ 100 rubs without exposing substrate (200 rubs for premium grade) |
Mortar resistance | No change |
Abrasion resistance | ≥ 200 L abrasion without exposing copper substrate |
Salt spray resistance | ≥ 1000 h without defects |
Resistance to accelerated weathering | 4000 h; ΔE ≤ 3, gloss retention ≥ 60% |
Damp heat resistance | No blistering, whitening, delamination, or corrosion |
Boiling water resistance | No blistering, shrinkage, or cracking |
The copper composite panels are ideally suited for staircases, facades, shading, and decorative architectural features.
Thanks to our advanced bonding technology, they offer outstanding durability and a distinctive aesthetic that evolves over time.
Its sleek modern surfaces and versatile finishes creates lasting contemporary looks.
Its unique and classical finish is highly favoured for museums and libraries.
Just like Titanium-zinc, its unique texture provides great possibilities for architects.